Grade 26
Datasheet
| ASTM Grade (UNS No.) | GRADE 26 (R52404) | |||||
|---|---|---|---|---|---|---|
| Chemical Composition (Max. values unless range is shown) |
(wt. %) | 0.08C; 0.03N; 0.25O; 0.30Fe; 0.08-0.14Ru; 0.015H | ||||
| TENSILE PROPERTIES | Guar.R.T. Min. | Typical Elevated Temperature Properties | ||||
| 93˚C (200˚F) | 204˚C (400˚F) | 315˚C (600˚F) | ||||
| Ultimate Strength | MPa (ksi) | 345 (50) | 393 (57) | 283 (41) | 221 (32) | |
| Yield Strength, 0.2% offset | MPa (ksi) | 276 (40) | 276 (40) | 166 (24) | 103 (15) | |
| Elongation in 51 mm (2") gage length | (%) | 20 | 28 | 41 | 38 | |
| Reduction in Area - Bar, Billet & Forging only | (%) | 30* | 40 | 55 | 75 | |
| OTHER MECHANICAL PROPERTIES | * bar, billet, forgings only | |||||
| Stress to Rupture in Time Shown | Stress | MPa (ksi) | 276 (40) | 240 (35) | 117 (17) | |
| Time-Hrs. at Temp. (˚C) | 10,000 (100) | 10,000 (150) | 1,000 (250) | |||
| Stress &Time to Produce Elongation Shown (creep) | Stress | MPa (ksi) | 209 (30) | 179 (26) | 103 (15) | |
| Time-Hrs. at Temp. (˚C) | 1,000 (25) | 1,000 (150) | 1,000 (250) | |||
| Creep | (%) | 1.0 | 1.0 | 1.0 | ||
| Charpy V-Notch Impact @ R.T. | Joules (ft-lbs) | 40 - 82 (30 - 60) | ||||
| Bend Radius | Under 1.78 mm (0.070") thick | 2.0 x Thickness | ||||
| 1.78 mm (0.070") and over | 2.5 x Thickness | |||||
| Welded Bend Radius | 2.5 - 3.0 x Thickness | |||||
| Nominal Hardness | 82 HRB | |||||
| PHYSICAL PROPERTIES | ||||||
| Nominal Beta Transus | °C (°F) | 913 (1675) | ||||
| Coefficient of Thermal Expansion 10-6/˚C (10-6/˚F) | 0-100˚C (32 -212˚F) | 8.6 (4.8) | ||||
| 0-315˚C (32-600˚F) | 9.2 (5.1) | |||||
| 0-538˚C (32-1000˚F) | 9.7 (5.4) | |||||
| 0-648˚C (32-1200˚F) | 10.1 (5.6) | |||||
| 0-816˚C (32-1500˚F) | 10.1 (5.6) | |||||
| Density | g/cm3 (lbs/in3) | 4.51(0.163) | ||||
| Melting Point, Approx. | °C (°F) | 1660 (3020) | ||||
| Electrical Resistivity @ R.T. | 10-6 ohm•cm (10-6 ohm•in) | 56 (22) | ||||
| Modulus of Elasticity – Tension | GPa (103 ksi) | 103 (15) | ||||
| Modulus of Elasticity – Torsion | GPa (103 ksi) | 41 (6.0) | ||||
| Thermal Conductivity | W/m•˚C (BTU/hr•ft•˚F) | 20.8 (12.0) | ||||
| Specific Heat | J/Kg•˚C (BTU/lb•˚F) | 520 (0.124) | ||||
| Weldability | Excellent | |||||
| Industry Specifications | ASTM - B265, B337, B338, B348, B363, B381, B861 and B862 | |||||